铣刨机刀具断裂原因分析与预防
摘 要：针对铣刨机刀具在实际施工中产生的刀具断裂问题，通过观察铣刨机刀具在使用过程中发生磨损和断裂失效的形貌，测试实体取样刀具的冲击功、硬度、金相组织，分析其磨损和断裂的原因，并提出提高耐磨性和防止断裂的措施，为提高铣刨机刀具的使用寿命提供了理论依据
关键词：铣刨机刀具；断裂；硬度；措施
中图分类号：U415.52 文献标志码：B
Analysis and Prevention of Cutter Fracture of Milling Machine
CHENG Juqiang1， WANG Xuejun2， SHEN Jinsong2
（1. School of Materials Science and Chemical Engineering， Xian Technological University， Xian 710032， Shaanxi， China； 2. Hubei Milalion Metallurgical Machinery Technology Co. Ltd.， Huanggang， 438000， Hubei， China）
Abstract： Aimed at the cutter fracture problem of milling machine during the construction， the causes of abrasion and fracture were analyzed by observing the shapes and testing the impact work， stiffness and metallographic structure of the cutter. Measures were proposed in order to improve the abrasive resistance and prevent the fracture， and theoretic basis for durability improvement was put forward.
Key words： milling machine cutter； fracture； stiffness； measure
0 引 言
路面铣刨机是公路及城市道路养护施工的专用机械，由于该设备具有效率高、施工工艺简单、铣刨深度易于控制、操作灵活、机动性能好、铣刨的旧料能直接回收利用等特点，因而被广泛应用于公路、道路、机场路面等沥青混凝土层的开挖翻修等养护施工中[12]。铣刨机施工时机械或液压传动带动铣鼓高速旋转，通过安装在铣鼓上的刀头切削路面以达到铣刨的目的。铣刨机的刀头在铣刨路面时会受到一定的冲击和磨料磨损，因此它是铣刨机主要的耐磨件和损耗件。为了提高铣刨机刀头的使用寿命，就要求其具有较高的强度、硬度、弯曲强度和耐磨性，以防止刀头在使用过程产生早期断裂、弯曲、变形和磨损失效。本文观察了铣刨机刀头工作时的失效形式，进行了试验与分析后，提出提高刀头耐磨性和防止断裂的措施。
1 试验方法
试验材料为商用铣刨机刀头...
|